Product details:

Porous nickel foam has been widely used in battery, supercapacitor and catalysis applications due to its light weight, high porosity and good stability. In catalysis field, the porous nickel foam is used as catalyst support which can reduce ion transfer resistance and facilitate the diffusion of gaseous products. In battery/supercapacitor field, the porous nickel foam can be used as substrate for in-situ hierarchical electrode preparation and thin film deposition. The as prepared electrode materials shows a better cycling performance, rate capability and larger charge/discharge capacity.

Specifications
Product SKU#	BR0112
Pack Size	1 piece
Material	Nickel
Dimensions	300 mm X 200 mm or customized
Thickness	1.6 mm or customized between 0.3~1.8 mm
Net weight	21 g
Surface density	320 g/m²
Porosity	97%, 110 pores per inch (100 PPI)
Pore size	~0.25 mm
Longitudinal tensile strength	≥95 N/cm²
Longitudinal elongation	≥ 5%
Transverse tensile strength	≥60 N/cm²
Transverse elongation	≥ 10%
Chemical Compositions	Ni+Co≥99.80% Fe≤0.02% C≤0.03% P≤0.2% Cu≤0.01% Si≤0.005% S≤0.008%

References:

1.Hierarchically Porous Urchin-Like Ni₂P Superstructures Supported on Nickel Foam as Efficient Bifunctional Electrocatalysts for Overall Water Splitting, ACS Catal. 2016, 6, 2, 714–721

2.Nickel foam-supported porous NiO/polyaniline film as anode for lithium ion batteries, Electrochem. Commun., Volume 10, Issue 9, September 2008, Pages 1288-1290

3. Anodic electrodeposition of a porous nickel oxide–hydroxide film on passivated nickel foam for supercapacitors, J. Mater. Chem. A, 2014,2, 7161-7164