PurionX AEM Premium Kit

The PurionX AEM Premium Kit provides a curated selection of high-performance anion exchange membranes for electrochemical, alkaline, and membrane research applications. This kit includes five different PurionX AEM models with varied thickness, conductivity, water uptake, dimensional stability, and chemical durability profiles, allowing researchers to evaluate and compare membrane performance under different experimental conditions.

Kit Contents

Model	Quantity	Size
PX-111	1 pc	20 x 20 cm
PX-113	1 pc	20 x 20 cm
PX-141	1 pc	20 x 20 cm
PX-142	1 pc	20 x 20 cm
PX-181	1 pc	20 x 20 cm

Total: 5 pcs/kit
Image for reference only

Specifications

Specification	PX-111	PX-113	PX-141	PX-142	PX-181
Membrane Type	Anion Exchange Membrane	Anion Exchange Membrane	Anion Exchange Membrane	Anion Exchange Membrane	Anion Exchange Membrane
Appearance	Clear, Semi-Transparent	Clear, Semi-Transparent	Clear, Semi-Transparent	Clear, Semi-Transparent	Clear, Semi-Transparent
Counter Ion	Hydroxide (OH⁻)	Chloride (Cl⁻)	Chloride (Cl⁻)	Chloride (Cl⁻)	Chloride (Cl⁻)
Thickness (dry)	50–55 um	~50 um	80–85 um	80–85 um	10–13 um
OH⁻ Conductivity at 23.0 °C	38–45 mS/cm	50–60 mS/cm	55–60 mS/cm	45–50 mS/cm	35–45 mS/cm
Weight per Unit Area	4.0–4.3 mg/cm²	4.0–4.6 mg/cm²	6.7–7.1 mg/cm²	6.7–7.1 mg/cm²	1.2–1.4 mg/cm²
Ion Exchange Capacity	2.2–2.5 meq/g	2.2–2.5 meq/g	2.2–2.5 meq/g	2.2–2.5 meq/g	2.2–2.5 meq/g
Tensile Strength at 23.0 °C, 50% RH	100–120 MPa	100–120 MPa	100–120 MPa	100–120 MPa	145–160 MPa
Young's Modulus at 23.0 °C, 50% RH	1500–2000 MPa	1500–2000 MPa	1500–2000 MPa	1500–2000 MPa	1500–2000 MPa
Elongation at Break at 23.0 °C, 50% RH	20–24%	20–40%	20–40%	20–40%	50–60%
Dimensional Swelling in H₂O at 23.0 °C	<10%	<6%	<6%	<8%	<5%
Water Uptake at 23.0 °C	50–60%	55–65%	55–65%	55–65%	45–55%
Alkaline Stability in 1 M KOH at 80 °C	>15,000 hours	>24,000 hours	>20,000 hours	>30,000 hours	>15,000 hours
Oxidation Stability in Fenton's Test at 80 °C	>36 hours	>36 hours	>60 hours	>72 hours	>24 hours

Applications

Anion exchange membrane research
Alkaline electrochemical systems
Fuel cell and electrolyzer research
Membrane conductivity and durability studies
Comparative membrane screening and material selection
Academic and industrial R&D applications

bettergy

PurionX AEM Premium Kit

Redox Flow Battery Membrane, RFB 8130, 25 cm X 25 cm

Redox Flow Battery Membrane, RFB 8130, 50 cm X 50 cm

Sintered Nickel Electrode Sheet for Alkaline Batteries and Electrolyzers, 150mm × 158mm × 0.76mm

Your Quote Cart

Your Quote Cart

Analyzing your theme...

Verifying your theme

Oops, your theme needs a little help!

We found a price field that our auto-setup tool couldn't configure.