PurionX AEM Premium Kit
Regular price
$ 620.95
Couldn't load pickup availability
Still have questions? Ask our experts!
PurionX AEM Premium Kit
The PurionX AEM Premium Kit provides a curated selection of high-performance anion exchange membranes for electrochemical, alkaline, and membrane research applications. This kit includes five different PurionX AEM models with varied thickness, conductivity, water uptake, dimensional stability, and chemical durability profiles, allowing researchers to evaluate and compare membrane performance under different experimental conditions.
Kit Contents
| Model | Quantity | Size |
|---|---|---|
| PX-111 | 1 pc | 20 x 20 cm |
| PX-113 | 1 pc | 20 x 20 cm |
| PX-141 | 1 pc | 20 x 20 cm |
| PX-142 | 1 pc | 20 x 20 cm |
| PX-181 | 1 pc | 20 x 20 cm |
Total: 5 pcs/kit
Image for reference only
Specifications
| Specification | PX-111 | PX-113 | PX-141 | PX-142 | PX-181 |
| Membrane Type | Anion Exchange Membrane | Anion Exchange Membrane | Anion Exchange Membrane | Anion Exchange Membrane | Anion Exchange Membrane |
| Appearance | Clear, Semi-Transparent | Clear, Semi-Transparent | Clear, Semi-Transparent | Clear, Semi-Transparent | Clear, Semi-Transparent |
| Counter Ion | Hydroxide (OH⁻) | Chloride (Cl⁻) | Chloride (Cl⁻) | Chloride (Cl⁻) | Chloride (Cl⁻) |
| Thickness (dry) | 50–55 um | ~50 um | 80–85 um | 80–85 um | 10–13 um |
| OH⁻ Conductivity at 23.0 °C | 38–45 mS/cm | 50–60 mS/cm | 55–60 mS/cm | 45–50 mS/cm | 35–45 mS/cm |
| Weight per Unit Area | 4.0–4.3 mg/cm² | 4.0–4.6 mg/cm² | 6.7–7.1 mg/cm² | 6.7–7.1 mg/cm² | 1.2–1.4 mg/cm² |
| Ion Exchange Capacity | 2.2–2.5 meq/g | 2.2–2.5 meq/g | 2.2–2.5 meq/g | 2.2–2.5 meq/g | 2.2–2.5 meq/g |
| Tensile Strength at 23.0 °C, 50% RH | 100–120 MPa | 100–120 MPa | 100–120 MPa | 100–120 MPa | 145–160 MPa |
| Young's Modulus at 23.0 °C, 50% RH | 1500–2000 MPa | 1500–2000 MPa | 1500–2000 MPa | 1500–2000 MPa | 1500–2000 MPa |
| Elongation at Break at 23.0 °C, 50% RH | 20–24% | 20–40% | 20–40% | 20–40% | 50–60% |
| Dimensional Swelling in H₂O at 23.0 °C | <10% | <6% | <6% | <8% | <5% |
| Water Uptake at 23.0 °C | 50–60% | 55–65% | 55–65% | 55–65% | 45–55% |
| Alkaline Stability in 1 M KOH at 80 °C | >15,000 hours | >24,000 hours | >20,000 hours | >30,000 hours | >15,000 hours |
| Oxidation Stability in Fenton's Test at 80 °C | >36 hours | >36 hours | >60 hours | >72 hours | >24 hours |
Applications
- Anion exchange membrane research
- Alkaline electrochemical systems
- Fuel cell and electrolyzer research
- Membrane conductivity and durability studies
- Comparative membrane screening and material selection
- Academic and industrial R&D applications