MSE PRO Lithium Nickel Manganese Cobalt Oxide, LiNi0.8Co0.1Mn0.1O2 NMC 811 Cathode Powder 500g

Ready to ship
SKU: PO5038
$ 380.95
$ 427.95 $ 380.95

Still have questions? Ask our experts!

Email +1 (520) 789-6673

MSE PRO™ Lithium Nickel Manganese Cobalt Oxide, LiNi0.8Co0.10Mn0.10O2 NMC 811 Cathode Powder 500g

Product Name: NMC 811 Cathode Powder 500g

SKU#: PO5038

CAS#: 346417-97-8

Package Size: 500g

Specifications:

Sample Name — NCM811 NCM811
Model — TOB-NMC-811-MJ-ZD TOB-NMC-811-MJ-ZD
Total Metal Content, Me % 60.00 ± 2.00 60.33
Ni Content % 50.50 ± 2.00 50.51
Co Content % 6.50 ± 1.00 6.51
Mn Content % 3.3 ± 1.00 3.31
Ni Molar Ratio mol% — 83.00
Co Molar Ratio mol% — 11.00
Mn Molar Ratio mol% — 6.00
Fe Impurity % ≤ 0.0100 0.0012
Na Impurity % ≤ 0.0300 0.0078
Ca Impurity % ≤ 0.0200 0.005
Cu Impurity % ≤ 0.0050 0.0005
Zn Impurity % ≤ 0.0050 0.0004
pH — ≤ 12.50 11.85
Li+ % ≤ 0.2000 0.1353
Dmin μm — 3.50
D10 μm ≥ 4.00 6.18
D50 μm 10.00–14.00 11.20
D90 μm ≤ 28.00 19.82
Dmax μm — 33.08
Tap Density g/cm³ ≥ 2.0 2.47
Specific Surface Area, SSA m²/g 0.20–0.70 0.47
Appearance — Dark blue powder, without agglomeration Pass
Physical Phase — Compare with JCPDS standard 70-4314, without unqualified phase In accordance with NMC XRD pattern
Coin Cell Type — — CR2430
First-Cycle Efficiency % ≥ 90 92.71
Capacity mAh/g ≥ 205 212.5
Voltage Range V — 4.30–2.8 V
The reported electrochemical performance was tested using a CR2430 coin cell under a voltage range of 4.30–2.8 V. Actual performance may vary depending on electrode formulation, coating conditions, electrolyte, separator, testing protocol, and cell assembly process.
Application Recommendations:
  • It is recommended to bake this NMC811 cathode powder in an oven at 125 degrees C for at least 6 hours before use. 
  • When this NMC811 cathode material is used with graphite anode, the designed full cell capacity is 190 ~ 194 mAh/g (0.5C, 4.2V - 3.0V)
  • Depending on application needs, please choose compatible electrolyte for building the battery cells.  