50g Super P Conductive Carbon Black For Lithium Ion Battery,  MSE Supplies

MSE PRO 50g Super P Conductive Carbon Black For Lithium Ion Battery

  • $ 8950

Qty (Each) Price (Each)
1 - 4 $ 89.50
5 - 9 $ 76.08
10 - 19 $ 67.13
20 - 99 $ 58.18
100 - 100+ $ 44.75

Product Descriptions:

The TIMCAL Super P Conductive Carbon Black has high purity and structure stability with a moderate surface area suitable in numerous battery applications as a conductive additive.

SKU#: BR0121
Package: 50 grams per bottle (Please contact us for volume discount if you need to order a higher quantity. Bulk order will be in bulk packaging. )
CAS Number: 1333-86-4

Product Benefits:

  • Increased battery safety
  • Fully compatible with most electrolyte systems
  • No dispersing agent is needed
  • Very high loading is possible
  • Cost savings on NMP and faster drying time 
  • High energy density
  • Improved power density
  • Cost reduction thanks to lower dosage needed
  • Improved “flexibility” of the electrode

Product Analysis

    Volatile content

    0.15%

    Toluene extract

    0.1%

    Ash content (600C)

    0.05%

    Grit content >45 microns

    5 ppm

    Grit content >20 microns

    25 ppm

    BET specific surface area

    62 m2/g

    Adsorption stiffness value

    32 ml/5g

    Moisture

    0.1%

    Density

    1.60 g/cm3

    Sulfur content

    0.02%

    pH

    10

    Iron

    5ppm

    Nickel

    1ppm

    Vanadium

    1ppm

    Package

    Sealed bottle

     Note: Please bake the SUPER P carbon black powder in an oven at 150 ~ 200°C to remove absorbed moisture before using it to make slurry for coating.

    References:

    Electrochemical properties of Super P carbon black as an anode active material for lithium-ion batteries, RM. Gnanamuthu, Chang WooLee, Materials Chemistry and Physics, Volume 130, Issue 3, 1 November 2011, Pages 831-834

    A comparative investigation of carbon black (Super-P) and vapor-grown carbon fibers (VGCFs) as conductive additives for lithium-ion battery cathodes, Inseong Cho, Jaecheol Choi, Kyuman Kim, Myung-Hyun Ryou and Yong Min Lee, RSC Adv., 2015,5, 95073-95078


    We Also Recommend
    High Purity (>95 wt%) Single-walled Carbon Nanotubes (Floating Catalyst Method), 1g,  MSE Supplies

    High Purity (>95 wt%) Single-walled Carbon Nanotubes (Floating Catalyst Method), 1g

    $ 23500
    Conductive Carbon Coated Copper Foil For Battery Research (260 mm wide 11 µm thick),  MSE Supplies

    MSE PRO 1 kg/roll Double Sides Conductive Carbon Coated Copper Foil For Battery Research (260 mm wide 11 µm thick)

    $ 37500
    MSE PRO 10 mL Gold (Au) Nanowire Dispersion - MSE Supplies LLC

    MSE PRO 10 mL Gold (Au) Nanowire Dispersion

    $ 99900 Save $ 11100
    100g Battery Grade Lithium Chips 12mm Diameter and 0.6mm Thick for Battery Research,  MSE Supplies

    MSE PRO 100g Battery Grade Lithium Chips 12mm Diameter and 0.6mm Thick for Battery Research

    $ 1,45000
    100g Battery Grade Lithium Chips 15.6 mm Diameter and 0.25 mm Thick for Battery Research,  MSE Supplies

    MSE PRO 100g Battery Grade Lithium Chips 15.6 mm Diameter and 0.25 mm Thick for Battery Research

    $ 1,45000