MSE PRO Porous Nickel Foam (300 mm L x 200 mm W x 1.6 mm T) for Battery and Supercapacitor Research
Product details:
Porous nickel foam has been widely used in battery, supercapacitor and catalysis applications due to its light weight, high porosity and good stability. In catalysis field, the porous nickel foam is used as catalyst support which can reduce ion transfer resistance and facilitate the diffusion of gaseous products. In battery/supercapacitor field, the porous nickel foam can be used as substrate for in-situ hierarchical electrode preparation and thin film deposition. The as prepared electrode materials shows a better cycling performance, rate capability and larger charge/discharge capacity.
|
Specifications |
|
| Product SKU# | BR0112 |
| Pack Size | 1 piece |
|
Material |
Nickel |
|
Dimensions |
300 mm X 200 mm or customized |
|
Thickness |
1.6 mm or customized between 0.3~1.8 mm |
| Net weight | 21 g |
| Surface density | 320 g/m2 |
| Porosity |
97%, 110 pores per inch (110 PPI) |
| Pore size |
~0.25 mm |
| Longitudinal tensile strength | ≥95 N/cm2 |
| Longitudinal elongation | ≥ 5% |
| Transverse tensile strength | ≥60 N/cm2 |
| Transverse elongation | ≥ 10% |
| Chemical Compositions | Ni+Co≥99.80% Fe≤0.02% C≤0.03% P≤0.2% Cu≤0.01% Si≤0.005% S≤0.008% |
References:
1.Hierarchically Porous Urchin-Like Ni2P Superstructures Supported on Nickel Foam as Efficient Bifunctional Electrocatalysts for Overall Water Splitting, ACS Catal. 2016, 6, 2, 714–721
2.Nickel foam-supported porous NiO/polyaniline film as anode for lithium ion batteries, Electrochem. Commun., Volume 10, Issue 9, September 2008, Pages 1288-1290
3. Anodic electrodeposition of a porous nickel oxide–hydroxide film on passivated nickel foam for supercapacitors, J. Mater. Chem. A, 2014,2, 7161-7164
We Also Recommend