MSE PRO LISICON LATP Solid State Electrolyte Membrane, 300um thick, 12mm diameter
Regular price
$ 215.95
Regular price
$ 253.95
Sale price
$ 215.95
Couldn't load pickup availability
Consumables Product
This consumable product is not available for refund or return
Still have questions? Ask our experts!
MSE PRO LISICON LATP Solid State Electrolyte Membrane, 300um thick, 12mm diameter, lithium aluminum titanium phosphate (LATP)
- SKU# ME0201
- Composition: LATP, Li1.3Al0.3Ti1.7(PO4)3
-
Size (Diameter): 12 mm +/- 0.3 mm
- Thickness: 300 um +/- 10 um
-
Lithium Ionic Conductivity: 2.75 x 10-4 S/cm at room temperature (25C)
- Relative Density: 95%
- Theoretical Density: 2.92 g/cm3
- Membrane Product Density: 2.77 g/cm3
- Flexural Strength: ~140 MPa
- Primary Crystal Structure: NASICON type LATP crystals
-
Applications: The unique properties of Ampcera™ LISICON lithium aluminum titanium phosphate (LATP) membrane solid state electrolyte materials make them ideal choices for all solid state lithium batteries, advanced Lithium-Sulfur, Lithium-Air, Lithium-Water batteries, etc. Ampcera™ LISICON (Lithium-ion Superionic Conductor) LATP membrane materials are used as solid state electrolytes or separators in advanced lithium batteries and other electrochemical devices.
- * All solid state electrolyte materials sold by MSE Supplies are under the trademark of Ampcera.
-
Li-O2 and Li-S batteries with high energy storage Peter G Bruce, Stefan A Freunberger, Laurence J Hardwick, Jean-Marie Tarascon Nat Mater 2012 Jan 15;11(1):19-29.
- Recent advances in all-solid-state rechargeable lithium batteries C Sun, J Liu, Y Gong, DP Wilkinson, J Zhang - Nano Energy, 2017 https://doi.org/10.1016/j.nanoen.2017.01.028
- Elaboration and characterization of a free standing LiSICON membrane for aqueous lithium air battery Laurent Puech, Christophe Cantau, Philippe Vinatier, Gwenaëlle Toussaint, Philippe Stevens
- Membranes in Lithium Ion Batteries Min Yang and Junbo Hou
- Li-ion transport in all-solid-state lithium batteries with LiCoO2 using NASICON-type glass ceramic electrolytes. Power Sources. 2009;189:365370. doi: 10.1016/j.jpowsour.2008.08.015. Xie J., Imanishi N., Zhang T., Hirano A., Takeda Y., Yamamoto O.