PMN-PT Single Crystals and Substrates, PMNT

  • $ 11900


PMNT (PMN-PT) Single Crystals and Substrates, Pb(Mg1/3Nb2/3)O3-PbTiO3

Standard specifications:

  • Cut types (crystal orientations): (001), (110), (111)
  • Single side polished, epi-ready, Ra < 1nm
  • PbTiO3 content (mol%) Type I: 28-30 (default), Type II: 30-34 (available upon request)
  • Sizes: 5 x 10 x 0.5 mm, 10 x 10 x 0.5 mm
  • Poling: Standard PMN-PT substrates are not poled. Poling service is available upon request. 

Customized sizes, shapes, orientation, poling directions are available upon request. Please contact us for quotation.

Specifications of PMN-PT single crystals

Parameter

PMN-PT

PMN-PT

cut-Type

Poling direction

Type I

Type II

 

 

PbTiO3 content (mol%)

28-30

30-34

(001)

<001>

Dielectric constant

4000-5500

5000-8000

Piezoelectric constant d33 (pC/N)

1200-1600

1500-2800

Piezoelectric constant d32 (pC/N)

-(600-900)

-(800-1100)

Electromechanical coupling factor k33

0.87-0.92

0.88-0.94

Phase transition temperature Trt (℃)

90-100

80-95

Curie temperature  Tc ()

130-140

140-160

Coercive field Ec (kV/cm)

2.0-2.5

2.0-2.5

Density (g/cm3)

8.1

8.1

 

 

 

 

 

Dielectric constant

2500-4000

3500-5000

(110)

<110>

Piezoelectric constant d33 (pC/N)

700-1100

1000-1800

Piezoelectric constant d32 (pC/N)

-(1100-1600)

-(1500-2200)

Piezoelectric constant d15 (pC/N)

2000-3500

3000-4500

<1-10>

Piezoelectric constant g15 (10-3Vm/N)

45-55

55-65

Piezoelectric constant d15 (pC/N)

3000-4500

4000-7000

<111>

Piezoelectric constant g15 (10-3Vm/N)

45-55

55-65

Electromechanical coupling factor k32

0.86-0.90

0.87-0.92

<110>

Curie temperature Tc ()

130-140

140-160

 

 

 

 

 

Available sizes

length: 1-70mm, width: 1-30mm

Available thickness

0.1-10 mm

Shapes

Plates, rings, rods, etc.

Surface finish

Fine grinding or polished

Electrodes (optional)

Silver, Gold

 

As a novel kind of piezoelectric materials, relaxor-based ferroelectric single crystals exhibit ultrahigh piezoelectric performances, which surpass largely those of conventional PZTs piezoelectric ceramics. Our company can provide three generations of relaxor-based piezocrystals, i.e. Pb(Mg1/3Nb2/3)O3-PbTiO3 (abbreviated as PMN-PT or PMNT), Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 (abbreviated as PIN-PMN-PT or PIMNT) and Mn doped Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 (abbreviated as Mn:PIN-PMN-PT or Mn:PIMNT) in large scale. High quality, large size and uniform crystals are available, which can satisfy various ultrasonic transducers in medical ultrasonic imaging, nondestructive examination and energy harvesting, solid-state actuators and composites such as magnetoelectric ones. The crystals have also good electro-optic properties and excellent pyroelectric properties, which can find application in the fields of electro-optic modulators in optical communications and pyroelectric devices in infrared detection and so on.

The main performance specifications are presented in the following tables. Various cut-type samples can be offered. Please contact us by email to discuss your requirements.

Reference Reading: 

Ferroelectrics: Applications
edited by Mickaël Lallart

relationship between crystal plane and poling direction PMNT