MSE PRO Casting Steel Grinding Balls
To better serve you, we would like to discuss your specific requirement, Please Contact Us for a quote.
MSE Supplies offers different types of casting steel grinding balls, with sizes ranging from 15mm to 130mm. Casting balls are produced by steel molds or sand box molds, with pouring ports, blisters and ring belts on the surface. As a primary grinding media, it is widely used in Cement Plants, Mines, Power stations, Chemical Industries, Coal mill and so on. Due to the high Cr content, the relative wear rates show a performance improvement of 25 – 30% and in the corrosive environments with low abrasion, the improvement could become 50% or more as compared with forged steel.
Any requirements, Please contact us for quote.
Chemical Composition of Casting Steel Grinding Balls
| SKU# | Materials | C% | Si% | Mn% | Cr% | Ni% | Mo% | Cu% |
| BA0560 |
ZQCr12 |
2.0-3.0 |
0.3-1.2 | 0.2-1.0 | 11-13 | 0-1.5 | 0-0.1 | 0-1.0 |
| BA0561 | ZQCr15 | 2.0-3.0 | 0.3-1.2 | 0.2-1.0 | 14-17 | 0-1.5 | 0-0.1 | 0-1.0 |
| BA0562 | ZQCr20 | 2.0-2.8 | 0.3-1.0 | 0.2-1.0 | 18-22 | 0-1.5 | 0-2.0 | 0-1.0 |
| BA0563 | ZQCr26 | 2.0-2.8 | 0.3-1.0 | 0.2-1.0 | 22-28 | 0-1.5 | 0-2.5 | 0-2.0 |
| BA0564 | ZQCr7 | 2.0-3.2 | 0.3-1.5 | 0.2-1.0 | 6.0-10 | 0-1.5 | 0-1.0 | 0-0.8 |
| BA0565 | ZQCr2 | 2.0-3.6 | 0.3-1.5 | 0.2-1.0 | 1.0-3.0 | 0-1.5 | 0-1.0 | 0-0.8 |
Specifications of Casting Steel Grinding Balls
| Nominal Diameter | Quantity/MT | Weight of single ball in average | Surface Hardness of High Chrome Balls | Endurance Impact Test |
| 15mm | 72549pcs | 13.8g | >60HRC | >10000 |
| 20mm | 30607pcs |
32.7g
|
>60HRC
|
>10000
|
| 30mm | 9069pcs | 110g | >60HRC |
>10000 |
| 50mm | 1959pcs | 510g | >60HRC |
>10000 |
| 60mm | 1134pcs | 882g | >60HRC |
>10000 |
| 80mm | 478pcs | 2091g | >58HRC |
>10000 |
| 100m | 245pcs | 4084g | >58HRC |
>8000 |
| 120mm | 142pcs | 7057g | >58HRC |
>8000 |
| 130mm | 115pcs | 8740g | >58HRC |
>8000 |
Features of Casting Steel Grinding Balls
- No deformation and breakage of the surface. Lower wear loss.
- Uniformity of the hardness from surface to core.
- High chrome casting balls and middle chrome casting balls could be more suitable in the corrosive environments.