Strontium Lanthanum Aluminate (SrLaAlO4) <001> Crystals and Substrates
Strontium Lanthanum Aluminate (SrLaAlO4) Crystals and Substrates
Strontium Lanthanum Aluminate (SrLaAlO4) Crystal and Substrate has similar structure to high-temperature superconductor Yttrium Barium Copper Oxide (YBCO), which makes it a good candidate for superconducting film because of the low lattice mismatch (~3.0%). It also has lower thermal expansion coefficient than other perovskite crystals, which allows the film to grow under lower temperature and produce high quality film. It is often used for growing superconducting film, microwave and high frequency application.
Technical Data
| SKU (mm) |
Single side polished: 5x5x0.5 (SU4101), 5x5x1 (SU4103), 10x10x0.5 (SU4105), 10x10x1 (SU4107) Double side polished: 5x5x0.5 (SU4102), 5x5x1 (SU4104), 10x10x0.5 (SU4106), 10x10x1 (SU4108) Please contact us for customization or bulk order |
| Crystal Structure | Tetragonal, a= 3.756 Å, c= 12.63 Å |
| Density (g/cm³) | 5.92 |
| Hardness (Mohs) | 6~6.5 |
| Melting Point (℃ ) | 1650 |
| Dielectric Constant | 16.8 |
| Polishing |
Single side polished, Double side polished |
| Roughness (Å) | ≤ 5 (5μm×5μm) |
| Orientation | <001> |
| Packaging | Sealed in class 100 clean bags packed in class 1000 clean room |